Synthesis of a novel phosphorus-nitrogen type flame retardant composed of maleimide, triazine-trione, and phosphaphenanthrene and its flame retardant effect on epoxy resin
Article
Huo, Siqi, Wang, Jun, Yang, Shuang, Wang, Junpeng, Zhang, Bin, Zhang, Bo, Chen, Xi and Tang, Yushan. 2016. "Synthesis of a novel phosphorus-nitrogen type flame retardant composed of maleimide, triazine-trione, and phosphaphenanthrene and its flame retardant effect on epoxy resin." Polymer Degradation and Stability. 131, pp. 106-113. https://doi.org/10.1016/j.polymdegradstab.2016.07.013
| Article Title | Synthesis of a novel phosphorus-nitrogen type flame retardant composed of maleimide, triazine-trione, and phosphaphenanthrene and its flame retardant effect on epoxy resin |
|---|---|
| ERA Journal ID | 1691 |
| Article Category | Article |
| Authors | Huo, Siqi, Wang, Jun, Yang, Shuang, Wang, Junpeng, Zhang, Bin, Zhang, Bo, Chen, Xi and Tang, Yushan |
| Journal Title | Polymer Degradation and Stability |
| Journal Citation | 131, pp. 106-113 |
| Number of Pages | 8 |
| Year | 2016 |
| Publisher | Elsevier |
| Place of Publication | United Kingdom |
| ISSN | 0141-3910 |
| 0144-2880 | |
| 1873-2321 | |
| Digital Object Identifier (DOI) | https://doi.org/10.1016/j.polymdegradstab.2016.07.013 |
| Web Address (URL) | https://www.sciencedirect.com/science/article/pii/S0141391016302178 |
| Abstract | In this paper, a novel phosphorus/nitrogen-containing compound (DMT) constructed by maleimide, phosphaphenanthrene and triazine-trione was successfully synthesized. The chemical structure of DMT was characterized by Fourier transform infrared spectroscopy (FTIR), 1H and 31P nuclear magnetic resonance (NMR). DMT was then blended with diglycidyl ether of bisphenol-A (DGEBA) to prepare a series of flame-retardant epoxy resins. The flame retardancy and combustion behavior were evaluated using limited oxygen index (LOI), vertical burning (UL94) and cone calorimeter test. The results indicated that DMT dramatically enhanced the flame retardancy of epoxy resin. When the phosphorus content was only 1.0%, the EP/DMT-1.0 sample had a LOI value of 35.8%, and achieved UL94 V-0 rating. The combustion parameters disclosed that DMT obviously weakened the heat release intensity. Compared with the neat EP sample, the peak of heat release rate (pk-HRR), average of heat release rate (av-HRR) and total heat release (THR) of EP/DMT-1.25 sample were decreased by 59.4%, 28.2% and 27.4%, respectively. The decreased av-EHC of EP/DMT thermosets indicated that DMT inhibited the gaseous phase combustion due to the gaseous phase quenching effect of phosphorus-containing free radicals derived from the decomposed DOPO group. The condensed phase studies indicated that DMT promoted the charring of EP matrix and formation of phosphorus-containing char layer with compact and intumescent structure. DMT exerted bi-phase flame retardant effect. © 2016 Elsevier Ltd |
| Keywords | Epoxy resin; Flame retardant; Maleimide; Phosphaphenanthrene; Triazine-trione |
| Contains Sensitive Content | Does not contain sensitive content |
| ANZSRC Field of Research 2020 | 401609. Polymers and plastics |
| Public Notes | Files associated with this item cannot be displayed due to copyright restrictions. |
| Byline Affiliations | Wuhan University of Technology, China |
Permalink -
https://research.usq.edu.au/item/yyy02/synthesis-of-a-novel-phosphorus-nitrogen-type-flame-retardant-composed-of-maleimide-triazine-trione-and-phosphaphenanthrene-and-its-flame-retardant-effect-on-epoxy-resin
48
total views0
total downloads1
views this month0
downloads this month